First edition. Non-destructive testing of steel tubes —. Part 1: Automated electromagnetic testing of seamless and welded (except. DIN EN ISO Non-destructive testing of steel tubes – Part 1: Automated electromagnetic testing of seamless and welded (except. Find the most up-to-date version of ISO at Engineering
|Published (Last):||19 January 2008|
|PDF File Size:||10.77 Mb|
|ePub File Size:||7.3 Mb|
|Price:||Free* [*Free Regsitration Required]|
This part of ISO can also be applicable to the testing of hollow sections. Users of British Stan- dards should make sure that they possess the latest amendments or editions.
Ultrasonic testing is the usual test method for all tube thicknesses and tube diameters; it is the preferred test method especially for thick-walled tubes. You may experience issues viewing this site in Internet Explorer 9, 10 or We have no amendments or corrections for this standard. It is applicable to the inspection of tubes with an outside diameter greater ej or equal to 4 mm, when testing with eddy current, and greater than 10 mm when testing with flux leakage method.
Please first log in with a verified email before subscribing to alerts. The minimum length of the longitudinal imperfection which is detectable is principally determined by the search coil arrangement and by the rate of change of section along the length of the imperfection.
It is applicable to the inspection of tubes with an outside diameter greater than or equal to 4 mm, when testing with eddy current, and greater than 10 mm when testing with flux leakage method. You may delete a document from your Alert Profile at any time.
ISO consists of the following parts, under the general title Non-destructive testing of steel tubes: If the document is revised or amended, you will be notified by email. The excitation frequency applied to the test coil determines the extent to which the induced eddy current intensity penetrates the tube wall. When using a single reference hole in the sample test pipe, the sample test pipe shall be passed through the inspection equipment with the reference hole, on successive runs positioned as requested in 6.
The faster, easier way to work with standards. We have no document history 100893-1 this standard. This website is best viewed with browser version of up to Microsoft Internet Explorer 8 or Firefox 3. This part of ISO specifies requirements for automated electromagnetic testing of seamless and welded steel tubes, with the exception of submerged arc-welded SAW ne, for verification of hydraulic leak-tightness in substitution of hydrostatic test.
Subscription pricing is determined by: It presents the UK view on standards in Europe and at the international level. Accept and continue Learn more about the cookies we use and how to change your settings.
It is recognized that longitudinal imperfections are not normally detectable unless they have a significant transverse component oblique. Ej 5 — Simplified diagram of magnetic flux leakage technique for the detection of transverse imperfections 6 Reference tube 6.
NOTE The bottom or the bottom corners of the notch can be rounded. This standard is also available to be included in Standards Subscriptions.
NOTE The pancake coils in a and b can have different forms, e. NOTE The magnetic transducers can take different forms, for example absolute and differential, depending on the equipment used and other factors. The means of introducing magnetic flux in a direction parallel to the major axis of the tube can be achieved by methods other than that shown in this figure. Take the smart route to manage medical device compliance.
Non-destructive tests are primarily used on pressure-retaining pipes for chemical, petrochemical and power station industries.
It supersedes BS EN Users are responsible for its correct application. Standards Subsctiption may be the perfect solution. The sides shall be nominally parallel and the bottom shall be nominally square to the sides. It is applicable to the inspection of tubes with an outside diameter greater than or equal to 4 mm, when testing with eddy current, and greater than 10 mm when testing with flux leakage method. A list of organizations represented on this committee can be obtained on request to its secretary.
BS EN ISO 10893-1:2011
International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. NOTE 1 It is recognized that there can be, as in the case of hydraulic testing under normal rn conditions, a short length at both tube ends which cannot be tested. It is the constant aim of BSI to improve the quality of our products and serv- ices. These operations shall be repeated for each segment coil.
BS EN ISO 钢管的无损检测–第1部分：用于验证水压密实性的无缝和焊接钢管(埋弧焊除外)自动电磁检测 – MBA智库文档
This publication does not purport to include all the necessary provisions of a contract. During the fIux leakage testing of tubes, the sensitivity of the test is at a maximum at the tube surface adjacent to the magnetic transducer and decreases with increasing tube thickness due to effective diminishing flux een from imperfections at the tube bore surface in relation to that at the external surface.
Your basket is empty. Please first verify your email before subscribing to alerts. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights.
Information on standards BSI provides a wide range of information on national, European and international standards through its Knowledge Centre. Please first verify your email before subscribing to alerts.
It is incorporated by Royal Charter. As the voice of the U. NOTE 2 In special cases, for 18093-1 testing hot tubes or using equipment contained within a continuous tube mill, a modified calibration or calibration checking procedure can be used, by agreement.